ARC S1HB: Corrosion Resistant Coating
An advanced, high build composite formulated to protect concrete and metal surfaces from corrosion and chemical attack. It is normally applied at a thickness of 1 - 2 mm (40 - 80 mils) per coat. However, greater single coat film thickness is achievable when spray applied. Non-shrinking, 100% solids. Color is Light Gray.
Click Here To Download:
•Datasheet: ARC S1HB -- Corrosion Resistant Coating
•ARC General Line Brochure
•ARC MCS Product Selector
•Concrete Composite Systems Selection Guide
•Brochure: Water And Wastewater Industry Solutions
An advanced, high build composite formulated to protect concrete and metal surfaces from corrosion and chemical attack. It is normally applied at a thickness of 1 - 2 mm (40 - 80 mils) per coat. However, greater single coat film thickness is achievable when spray applied. Non-shrinking, 100% solids. Color is Light Gray.
ARC S1HB is a high viscosity, high performance composite lining that is designed to be spray applied but may also be applied by brush. ARC S1HB allows for uniform coverage over rough surfaces and yields excellent barrier properties for long-term corrosion and chemical resistance in immersion exposures. The cured ARC S1HB provides a barrier film with unrivaled adhesion and resistance to corrosion.
Technical Data:
Dry Temperature Dry (Min/Max) -20 F (-29C) to 175 F (80 C)
Wet Temperature (Min/Max) -20 F (-29C) to 125 F (52 C)
Compressive Strength - kg/cm2 - Mpa (psi) 870 - 84 (12400)
Flexural Strength - kg/cm2 - Mpa (psi) 420 -41 (6,000)
Tensile Strength - kg/cm2/Mpa (psi) 385 - 38 (5,550)
Tensile Adhesion - kg/cm2 - Mpa (psi) Greater than 28- 2,8 (400)
Impact Resistance - nt m (in. lbs.) > Concrete
Shore D Hardness 85
Click Here To Download:
•Datasheet: ARC S1HB -- Corrosion Resistant Coating
•ARC General Line Brochure
•ARC MCS Product Selector
•Concrete Composite Systems Selection Guide
•Brochure: Water And Wastewater Industry Solutions