ARC 858: Ceramic Rebuilding Compound

An advanced ceramic composite for the repair and protection of all metal surfaces subjected to erosion, corrosion and chemical attack. The ARC 858 is formulated for light abrasive, erosive and corrosive environments where metal loss is often repaired by more conventional and costly weld overlay. It can be used either to rebuild eroded metal surfaces or to provide a wear resistant surface.

Technical Data

• Dry Temperature Dry (Min/Max) -20 F (-29C) to 320 F (160 C)
• Wet Temperature (Min/Max) -20 F (-29C) to 160 F (70 C)
• Compressive Strength - kg/cm2 - Mpa (psi) 920 - 92 (13,000)
• Flexural Strength - kg/cm2 - Mpa (psi) 620 - 62 (8,800)
• Tensile Strength - kg/cm2/Mpa (psi) 430 - 43 (6,100)
• Tensile Adhesion - kg/cm2 - Mpa (psi) Greater than 140 - 14 (2,000)
• Shore D Hardness 85