ARC S2: Ceramic Reinforced Erosion Resistant Coating

An advanced ceramic composite for the resurfacing and protection of all metal surfaces. ARC S2 is a low viscosity composite that is designed to be spray applied but may also be applied by roller or brush. ARC S2 is formulated for the resurfacing of metal components subjected to extreme corrosive or severe fluid flow conditions. It is normally applied at a thickness of 250 microns (10 mils) per coat.

Technical Data:

Dry Temperature Dry (Min/Max) -20 F (-29C) to 175 F (80 C)
Wet Temperature (Min/Max) -20 F (-29C) to 125 F (52 C)
Flexural Strength - kg/cm2 - Mpa (psi) 770 - 75 (11,000)
Tensile Strength - kg/cm2/Mpa (psi) 470 - 47 (6,700)
Tensile Adhesion - kg/cm2 - Mpa (psi) Greater than 140 - 14 (2,000)
Water Vapor Permeability (meteric perm-cm - Perms) 5.60E-04
Salt Fog >20,000 hrs
Shore D Hardness 85